Cell Solution CLIMA 6,7

PATENTED GERMAN FIBRE TECHNOLOGY

Cell Solution CLIMA fibre 6,7

Botanic Fiber

Cell Solution® Clima fibers are natural cellulosic manmade fibers. The main raw material is wood pulp from non-endangered trees, and the additive paraffin is refined plant oil.

Functionality
Cell Solution® Clima technology creates a “micro heat accumulator”, which acts as an extraordinary temperature buffer between warm and cool.

PCM
Cell Solution® Clima fiber is a PCM (Phase Change Material) micro composite of the latest fiber manufacturing generation with advanced thermo regulating features when compared to the classic phase change materials. Via a patented spinning process, paraffin is embedded in crystalline and tear resistant functional lyocell fibers. Thus producing unequaled many micro composite accumulators per unit of cellulosic fiber, using which the textile imparts enhanced comforting features.

Temperature Control
PCM Textiles manufactured with Cell Solution® Clima adjust to the skin’s comfort temperature. It can absorb excessive body heat, and when the temperature drops, dispense it again. Thus temperature regulation is assured, providing extraordinary wearing comfort and excellent microclimate.

Cell Solution® Climafibers provide high energy absorbtion (more than 92 Joules per gram of fiber for 6,7 dtex and more than 50 Joules for 2,3 dtex fibers). Thus stable temperatures can be achieved within a specific time period.

Moisture Control
The structure of the cellulosic fiber results in an optimal bodyclimate because of the fiber’s excellent moisture absorbing properties. Synthetic fibers do not absorb any moisture.

Additional features
Cell Solution® Clima fibers can be easily processed in to textiles and have consistent dyeability when following the recommended processing/finishing method.

Even though the fiber is heavily loaded with PCM, the fiber surface remains smooth. Thus making it insensitive to mechanical and chemical forces. All of this provides functional performance and allows washing of fibers and textiles.

Cell Solution® Clima fibers can be used in nonwoven applications or spun into yarns.

Range of application
In all areas where comfort and regulation of one’s climate is desired:

  • Mattresses
  • Quilts
  • Pillows
  • Blankets
  • Bedlinen

Garments where the “temperature buffer” enhances comfort and performance:

  • Army
  • Police
  • Sportswear
  • Workwear
  • Formal suiting
  • Casual suiting
  • Socks
  • Gloves

CLIMA fibre cell structure 6,7Clima Fibre 6,7 comfort zone chart

Cell Solution® CLIMA 6,7 dtex.

Data sheet

Cellulose fibre with thermoregulating properties produced according to the Lyocell – process

Fibre composition in conditioned state (given in % by weight):

Cellulose > 46 %
Stabilized paraffin (defined melting point) app. 36 %
Organically modified mineral (layered silicate) 5 – 6 %
Finished content <0,5 %
Moisture <10 %
Titre dtex 6,7 ± 10%
Tenacity, conditioned cN/tex > 15
Tenacity, wet cN/tex > 12
Elongation, conditioned % 12 – 16
Elongation, wet % 14 – 19
Loop tenacity cN/tex 3 – 5
Wet modulus cN/tex ± 60
Whiteness > 30
Staple length mm 60 ± 10%
Melting point (peak) 29-33°C / 84-91°F
Thermal decomposition >175°C/350°F
Ignition point >200°C/390°F

Due to the large amount of n-paraffin in the fiber, longer exposure of the product in dry state to temperatures above 100°C/210°F has to be avoided or will result in vaporizing of paraffin.

Storage capacity in accordance with DIN 51007 (DSC)   > 75 Joule per Gram.